[MW:1749] Re: 1747] Re: Use of 316L for steam service

I understand that the core material is SS316L and what is the jacket
material?
What is core fluid and what is jacket fluid?
What is ambient environment? Any leakage or any other gaseous hazard?
I told you for additional info.
Please appreciate that I need to have the total picture.

I think no problem. You can go ahead.
Your argument may be correct if there is Cl2 or Fl2 environment.
If core fluid is compatible to SS316L, are you bothering for steam?

Regards,

Bibek Bhattacharyya.

"Faigal Fernando
Agbanawag"
<faigal.agbanawag To
@czfp.com> <materials-welding@googlegroups.com
Sent by: >
materials-welding cc
@googlegroups.com
Subject
[MW:1748] RE: 1747] Re: Use of 316L
03/11/2009 03:51 for steam service
PM


Please respond to
materials-welding
@googlegroups.com

Dear sir,

There was a recommendation that a 316L material be use for inner piping
of jacket piping. I am trying to put up an argument that there could be
some problem in the usage of this material. The service temperature is
233F and the steam is 338F, the pressure are 15 and 75 respectively.

Thanks and regards.

Faigal Fernando Agbanawag
Sr. Piping Engineer
Clough ZFP
T+966 3 8828818 Ext: 241
F+966 3 8828622
M+966 (0) 507780576

Disclaimer: This email and any files transmitted with it are confidential
and intended solely for the use of the addressee(s) named herein. If you
are not the intended recipient or addressee, you should not use,
disseminate, distribute, copy or alter this email. Any views or opinions
presented in this email are solely those of the author and might not
represent those of "CZFP".
Warning: Although reasonable precautions have been taken to ensure no
viruses are present in this email, "CZFP" cannot accept responsibility for
any loss or damage arising from the use of this email or attachments. If
you have received this electronic mail message in error, please contact the
sender directly.
-----Original Message-----

From: materials-welding@googlegroups.com
[mailto:materials-welding@googlegroups.com] On Behalf Of
Bhattacharyya_Bibekananda@ke0.grp.kaneka.co.jp
Sent: Wednesday, March 11, 2009 9:13 AM
To: materials-welding@googlegroups.com
Cc: materials-welding@googlegroups.com
Subject: [MW:1747] Re: Use of 316L for steam service

Please indicate the steam pressure and temperature... Also, the
frequency
of use... At a glance, the material can be used but for further
analysis,
more info is needed.
B36.19M and B36.10M.
For large bore SS pipes, you can specify thickness from 36.10M, based on
your requirement.
You can refer or use "ASME B31.3 Calculator" at
www.cheresources.com/software.shtml.

Kind Regards,
Bibek Bhattacharyya.

"Faigal Fernando

Agbanawag"

<faigal.agbanawag
To
@czfp.com>
<materials-welding@googlegroups.com
Sent by: >

materials-welding
cc
@googlegroups.com

Subject
[MW:1746] Use of 316L for steam

03/11/2009 03:01 service

PM

Please respond to

materials-welding

@googlegroups.com

Dear All,

Can anybody please tell me if 316L for steam service is tolerable or
not.
Is there any reference in B36.19M with regards to this criterion or in
any
industry codes.

Thanking you all in advance.

Faigal Fernando Agbanawag
Sr. Piping Engineer
Clough ZFP

T +966 3 8828818 Ext: 241

F +966 3 8828622

M +966 (0) 507780576

Disclaimer: This email and any files transmitted with it are
confidential
and intended solely for the use of the addressee(s) named herein. If you
are not the intended recipient or addressee, you should not use,
disseminate, distribute, copy or alter this email. Any views or opinions
presented in this email are solely those of the author and might not
represent those of "CZFP".

Warning: Although reasonable precautions have been taken to ensure no
viruses are present in this email, "CZFP" cannot accept responsibility
for
any loss or damage arising from the use of this email or attachments. If
you have received this electronic mail message in error, please contact
the
sender directly.

--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---