[MW:1809] Re: Query on SMAW electrode selection for API 5L X65

By Materials & Welding
For mainline, we used 40" dia X65/1" WT root 6010, remaining 8018G.
 
Regards,
S.Senthilkumar

--- On Mon, 23/3/09, hakan sitem <hakansitem@yahoo.com> wrote:

From: hakan sitem <hakansitem@yahoo.com>
Subject: [MW:1796] Re: Query on SMAW electrode selection for API 5L X65
To: materials-welding@googlegroups.com
Date: Monday, 23 March, 2009, 1:43 PM

Hi, pls note the following applications;
Mainline Welding:
 

Steel Grade

Root Pass

Hot Pass

Filling

Cap

 

 

 

 

 

X42/X52

Pipeweld 6010

Pipeweld 7010

Pipeweld 7010

Pipeweld 7010

X60/X65

Pipeweld 6010

Pipeweld 8010

Pipeweld 8010

Pipeweld 8010

X70

Pipeweld 6010

Pipeweld 9010

Pipeweld 9010

Pipeweld 9010

 

 

 

 

 

 


 
Weld area strengths and properties should be observed. So we will focus on  "Total Weld Metal Area" and also HAZ for the required
--- On Sun, 22/3/09, ARI <ariv2k@gmail.com> wrote:
From: ARI <ariv2k@gmail.com>
Subject: [MW:1792] Re: Query on SMAW electrode selection for API 5L X65
To: materials-welding@googlegroups.com
Date: Sunday, 22 March, 2009, 9:43 AM

Hi,
 
Using E6010-G would keep the dilution level as minimum, but at the same time, it wouldn;t give the UTS equal to Parent metal UTS for API5L X65?

Regards,
 
Ari
 
On 3/21/09, babu k <kbabupsg@gmail.com> wrote:

Hi,
 
Put it in simple words, the use of E6010-G is to keep the dilution level to be minimum ; 
 
Thanks & Regards,
 
K.Babu
Singapore
 

 
On Thu, Mar 19, 2009 at 6:15 PM, Ari <ariv2k@gmail.com> wrote:

Dear All,

Can you please advise, why E6010-G (root) & E-7010-P1 (hot/fill) are
used for Oil pipelines(Sour) containing parent material of API 5L X65.
Since these type of PQR/WPS are being approved by most of the
Company.

As, X65 has an YS of 65,000 Psi, whilst the electrodes used E6010 has
YS of  48,000 Psi, and E-7010-P1 has YS of 60,000 psi. By using both
of these electrodes the weld metal strength would not exceed  YS
60,000 psi.

How its acceptable to keep the low weld metal strength(<YS 60,000 Psi)
than the parent metal (= YS 65,000Psi).

Thy suppose to use E8010 for root and E8018 for hot/fill, for API 5L
X65 materials, which only would give the equivalent WM strength.

As we all know that overmatching weld metal strength causes gross
section yielding in the pipe, whereas Undermatching weld metal
strength will cause straining of the weld.

Your advise/suggession, based on experience is appreciated.

Regards,

Ari






New Email addresses available on Yahoo!
Get the Email name you've always wanted on the new @ymail and @rocketmail.
Hurry before someone else does

Connect with friends all over the world. Get Yahoo! India Messenger. --~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

By Materials & Welding
Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...
Post a Comment
Read more