[MW:1778] Re: Socket welding gap

By Materials & Welding
we have tried with matchsticks(without heads) and it worked well.

On Wed, Mar 18, 2009 at 12:52 AM, Sudheer Babu <sudheerbabun@gmail.com> wrote:
We were using cardboard sheet (circular ) to maintain the gap during Pigtail welding in one of our projects It was mandatory to maintain required Gap of 1.6mm to counter thermal expansion.  The cardboard sheets used to get burned off at high temperatures during pre-commissioning.
This was acceptable to our client but not sure if this will be case with every client.
 
Regards
 
NSB

On Tue, Mar 17, 2009 at 10:46 PM, Salvador, Camilo <cafsss@gmail.com> wrote:

We're welding Socket-welding fittings from 3/8 to 2", and we have
trouble with the internal offset  requested on ASME B31.3.

Our client hasn't accepted the usual method, which consist in use a
"elastic welding spacer" (US patents related: 4,505,420 or 4,346,918
or Google: gap-a-let).

Is there another method, e.g.: an external device - that can be used
for this welding, ensuring the correct gap [1.6 mm] ?



I know that's a materials related forum, but I'm sure you guys can
help me.

Regards.
Salvador.






--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more