Your photos clearly shows endless amount pores in the weldThe main cause for porosity in aluminum is hydrogen, which has very high solubility in molten aluminum but very low solubility in solid. Hydrogen gas is therefore evolved as the weld pool solidifies. If the cooling rate is too high, the gas remains in the metal in the form of porosity. Thus, any compound containing hydrogen and contaminating the filler wire or work surface can cause porosity.
Oil, moisture or other contaminants may be present on the filler wire. In addition, the oxide layer of aluminum tends to get hydrated and improper cleaning of the oxide layer immediately preceding welding could be a cause for porosity. Ensuring that the plate is clean before welding and switching to clean, high quality electrodes will reduce the likelihood of forming porosity.
The amount of porosity depends on how fast the weld pool solidifies. Increasing the welding current and/or decreasing the travel speed will increase the heat input, and help retard the cooling rate allowing gases to escape from the weld pool and thereby reducing the risk of porosity.
Filler wires should ideally be kept in their packaging until needed; wire that is left out ion open workshop conditions will absorb moisture into its oxide layer. It is advisable when welding aluminum to wipe each wire prior to use with a clean cloth dipped in acetone.Sridhar.Pre heat the weld and HAZ area to mimnimum150 deg. C to eliminate hydrogen pores. Once you overcome it, the tests
will pass through.On Monday, 7 May, 2018, 4:16:16 PM IST, Hani Al Masry <hanyonalfy@gmail.com> wrote:Dear experts--regarding A/M Subject kindly advice why the PQR Test had been failed two times even this WPS/PQR Approved before and we just tried to copy itall welders 2 times failed in root bend / tension some times not reach 250 MPA as required (2 root bend + 2 root face + 2 tensile testing are required)the lab said first time there are porosity
and inclusions but even 2nd test was failed (attached photos for your reference)BASE METAL : AA 5083 H 321FILLER METAL : ER 5356Joint Preparation: - Single V CPJ
Weld Layer
WELDING PROCESS
WELDING POSITION / DIRECTION
ELECTRODE(S)
GAS SHIELD
GAS FLOW RATE
lit/min.
AMPS
VOLTS
WELDING SPEED mm./min.
FLUX
WFS
M/Min.
Mode of Metal transfer for MAW
SIZE
mm
TRADE NAME
POLARITY
1
GMAW
3G
1.2
AUTO ROD 5356
DCEP
ARGON 99.99%
15-25
120-180
18-26
12-20
NA
8.5
Pulse transfer
2
GMAW
3G
1.2
AUTO ROD 5356
DCEP
ARGON 99.99%
15-25
120-180
18-26
120 - 140
NA
8.5
Pulse transfer
Back weld
GMAW
3G
1.2
AUTO ROD 5356
DCEP
ARGON 99.99%
15-25
120-180
18-26
100 - 110
NA
8.5
Pulse transfer
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
Visit this group at https://groups.google.com/group/materials-welding .
For more options, visit https://groups.google.com/d/optout .--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
Visit this group at https://groups.google.com/group/materials-welding .
For more options, visit https://groups.google.com/d/optout .
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment