Re: [MW:24697] Carbon/Manganese pressure vessel ASME VIII, Crack after PWHT

Most probably cold cracking. Hydrogen bake out treatment should have been implemented.

Sent from my BlackBerry 10 smartphone.

From: Zakaria ghrab Sent: Πέμπτη, 7 Απριλίου 2016 - 05:48 To: materials-welding@googlegroups.com Reply To: materials-welding@googlegroups.com Subject: [MW:24636] Carbon/Manganese pressure vessel ASME VIII, Crack after PWHT

Dear Experts,

 Need your support for one issue :

Construction code : ASME VIII Div 1

Pressure vessel fabrication.

Material: A516 Gr 70N

Thickness : 48 mm

Welding process : SAW/FCAW;

Joint design: X

For one of Circulaire joints, UT & TOFD performed before PWHT and result was conform.

After PWHT, One crack around 40mm lenght, detected centerline of the weld surface in the internal side of vessel.

In my assessment, 

• crack may be hydrogen crack dur to no control of interpass temperature and heat input or due to Carbon picked up from parent metal to weld zone and due to lower manganese concentration, Crack occurs.
  
• May be Crack taked time to occurs (it's possible that crack present after 03 days of weldment, please confirm to us) and in this case may be NDE performed before crack that's why NDE reports before PWHT present conform result.

Please your support & Feedback experience and what you propose as corrective / Preventive actions.

--

Thanks and Regards, ?

-----

زكرياء غراب
GHRAB Zakaria 

EA2C Tunisia.

Tunisia : +216 96 635 805

Morocco : +212 6 06 58 88 56

Bénin : +229 97 128 387


Yesterday is the past, tomorrow is the future; and today? Today is the present, the gift: Enjoy it!

--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAD8EeB21thvysyFQ3zyYybv0MquE8WanbnjW-W%3Dcpp7DE2vUaw%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.