Dear Sir,
-- Pl refer PG 19 of ASME SEC I OR UHA 44 of ASME SEC VIII DIV 1 before deciding Heat treatment . The strain and service temperature , both shall be considered .
for 4.06 mm thk, Blat of air should suffice and so the distortion etc
Do a mock up test and plan accor
On Tuesday, March 15, 2016 at 11:19:42 AM UTC+5:30, kannayeram gnanapandithan wrote:
On Tuesday, March 15, 2016 at 11:19:42 AM UTC+5:30, kannayeram gnanapandithan wrote:
Experts comments on the following for any precautionary measured to be takenTube Matl--- ASS 316LDimension--- Dia 38.1 X 4.06 mm thickR/D ratio=1Cold bending followed by Solution Annealing ( Water or Air quencing, advice required to choose Air or Water),Followed by IGC as per A262 Practice ETHANKS & BEST REGARDS,KG.PANDITHAN, IWE, AWS-CWI, CSWIP 3.1,CONSULTANT-WELDING & QUALITY
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/e9019041-bd14-450e-b9d2-7759bd00ec6a%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.
Comments