Dear Dipak
As per my knowledge UT and PAUT is not possible due to austenite grain structure.
On Apr 23, 2015 5:40 PM, "deepak cb" <dcbvjs@gmail.com> wrote:
-- I would like to take NDT on Weld joints of 316 Pipe material Sch 10s. As per the site condition X-ray cant be used. And gamma source is also not available. Is there any other way. I mean Manual Ut or PAUT? Does the minimum thickness will be a problem if i go for Manual UT? please advise--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/e1717216-36c2-4159-b1be-bd02fc1629fe%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CABhgLaz%3Drx%3DK%2BDk0JuZRdpbJLAPyb8fJVUXUB5-5f4mdZNMPKA%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment