Re: [MW:23023] Dillmax 690 weld cracks

hi..thanks.

read these docs...no clue on reasons on where we went wrong?

On Monday, 30 March 2015 14:27:08 UTC+5:30, Lalu r p wrote:

Hi,

With all high strength, quenched and tempered fine grained structural steels, DILLIMAX steels are susceptible to cracking (Cold cracking) in the weld area if the conditions are unfavorable AND these cracks may not appear until 48 hours after welding. In order to ensure that the tensile strength of the weld metal fulfills the requirements of the base metal, the heat input and interpass temperature must be limited during welding. Please refer the attached data sheets for more information.

regards,
LALU
LINKS MIDDLE EAST
ABU DHABI, UAE

On Mon, Mar 30, 2015 at 11:00 AM, RK <krishn...@gmail.com> wrote:
Hi..

We have used Dillimax 690PE material for our penstocks under construction.
Experienced delayed cracking in welds (after a month or so) in all most all the welds...in all 3 welding processes used SAW, SMAW, FCAW...cracks are only in the welds!!!
Process is PH 100-150 DegC, Interpass 200 Deg C and DHT 200-250 DegC for 3 hrs.
Can anyone have any idea what could be the reasons?? we are in soup...and not able to proceed further..

rgds

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To post to this group, send email to material...@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/71e1545b-e44d-4786-9afe-6e6d53a90504%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/f5ed1c45-e010-4b87-ba26-0b98c1d85e72%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

[MW:36169] Cold Bending Qualification

Dear Experts, Can anyone share the inspection requirements or a qualification procedure for cold bending? Our client spec states only the requirements for induction bending and would like to know your opinion on the cold bend inspection requirements. The code of construction is B31.3, Max. 5D bends, A106 SS 316L. Thanks in Advance. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion visit https://groups.google.com/d/msgid/materials-welding/1be61cc3-e9c9-4a5f-834d-e8485e248432n%40googlegroups.com .

[MW:30043] Weep hole

If weep hole is not provided in dummy pipe before welding What will happen??? -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da251ee6-fa7f-4851-b876-cdb3834ae341%40googlegroups.com .

Materials & Welding

Search This Blog