FCAW Process Filler wire E71T-1C does this come under low hydrogen electrode category?
ASME Sec IIC-SFA 5.20
A8.2.4 Most flux cored electrodes deposit weld metal having diffusible hydrogen levels of less than 16 mL/100 g of deposited metal. For that reason, flux cored electrodes are generally considered to be low hydrogen. However, some commercially available products will, under certain conditions, produce weld metal with diffusible hydrogen levels in excess of 16 mL/100 g of deposited metal. Therefore it may be appropriate for certain applications to utilize the optional supplemental designators for diffusible hydrogen when specifying the flux cored electrodes to be used.
Question no -01
In the engineering drawing for welding the anchor chair of atmospheric storage tank in the field, it is specified to "Weld with low hydrogen electrode".
Can we weld with FCAW process using E71T-1C filler wire, ASME Sec IIC-SFA 5.20 for above mentioned application? The EN10204 3.1 certificate for the filler wire shows hydrogen test results performed on the deposited weld metal, a maximum of 3.0 ml/100g.
Question no -02
Is there any difference between "low hydrogen weld deposit" and "low hydrogen electrode" in the light of ASME Code?
Note:-
Also Find attached files..
Please kindly provide code reference...
Thank you.
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAFoQ_neZ4YX676Ra1%3DZ5iGYc6d-w2u-%2B2gWZE1rgBFU5Vro26g%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment