RE: [MW:5321] Peaking & Bending Measurement of Welded Joints in Cylindrical Storage Tanks....

By Materials & Welding
You can make a template from a steel sheet / scrap plate with radius of template equal to your tank radious with an arc length of aprx 1 mtr. place this on your tank and if you are getting greater than 12mm gap, needs rectification. Similar way use 1 mtr steel rule as straight edge to check verticality.

Your 4th point itself is an answer to your query. How do you intended to check verticality and circularity?


Sent from my Nokia phone
-----Original Message-----
From: jose seban
Sent: 31/05/2010 6:40:27 pm
Subject: [MW:5320] Peaking & Bending Measurement of Welded Joints in Cylindrical Storage Tanks....

Dear Friends,

I am making fixed roof cylindrical oil storage tanks as per Indian
Standards IS-803.In section 9.3.5 it is mentioned about circularity
and shape.There it is mentioned about verticality & circularity
tolerences.Also it is mentioned about peaking and bending of welds
there..

1.Peaking of vertical weld joints measured over an arc length of 1 m
shall not exceed 12 mmm.

2.Bending of horizontal weld joints measured by a straightedge of 1 m
length shall not exceed 12 mm.

My questions are..

1.What is meant by this peaking and bending there?
2.How we will measure these factors?
3.How would the unit "millimetre" will come for these factors
measurement?
4.Is these 2 measurements are important in tank fabrication,if I am
checking vericality & circularity properly?


Regards,

Jose Sebastian,
Quality Manager,
Adani Power Limited,
Gujrat,India.
Mob:+919687660525

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more