By Materials & Welding
dear Mr. Prasad
Appriciate if you can give clarification, if desired with an example.

___________________
From: materials-welding@googlegroups.com [materials-welding@googlegroups.com] On Behalf Of N VENKATESWARA PRASAD [weldengr.velosi@gmail.com]
Sent: Tuesday, May 25, 2010 6:54 PM
To: materials-welding@googlegroups.com
Subject: Re: 5244] WPS thickness limits with PWHT

The Thickness restriction will be relaxed as per QW 403.6 when PWHT is more than upper transition temp. when impact is the requirement. When Impact is requiremnt the with out PWHT qualificaiton reange is T to 2T where with PWHT above Transisiton temparature it will be 1/2 t to 2T.

regards

On Fri, May 21, 2010 at 11:06 AM, Bathula Raghuram (Mumbai - PIPING) <R.Bathula@ticb.ovcom> wrote:
Please don't reply to an existing thread while posting new query and use appropriate subject line, members are requested to follow, as many queries are deleted during moderation.

regarding your query, Yes max thickness qualified is restricted to 1.1T where PWHT exceeding upper transformation temp for ferrous metals, except P7,8 and 45, refer QW 407.4

________________________________
From: materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com> [mailto:materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>] On Behalf Of Subrata Das
Sent: Friday, May 21, 2010 11:29 AM
To: materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>
Subject: RE: [MW:5206] NDT after PWHT

Dear all
Is there any limitation of thickness criteria as per Sec. IX whether WPS qualified in PWHT or Normalizing /Annealing.


Thank you with best regards!

Subrata Das
P.K. Tubes & Fittings Pvt. Ltd.
A458 Chopanki Industrial Area
Distt:- Alwar , Bhiwadi ( Rajasthan ) India
01493-516620,516608 Fax:- 01493-516618
Mob:- +91-9828160168

From: materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com> [mailto:materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>] On Behalf Of Arunachalam A
Sent: Friday, May 21, 2010 10:56 AM
To: materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>
Subject: Re: [MW:5205] NDT after PWHT

I think UHA-33 require RT examination after PWHT. No other ASME paragraphs specify the RT after PWHT.
arun

On Fri, May 21, 2010 at 8:34 AM, GOPU NAIR <gopunair5343@yahoo.com<mailto:gopunair5343@yahoo.com>> wrote:
ASME SEC. VIII DIV. 1 does not ask for RT of weld joints after PWHT. Please check your customer specification which may require the joints to be radographed after PWHT.

Gopu Nair

--- On Thu, 20/5/10, Luis Albanes <ing_albanes@yahoo.com.mx<mailto:ing_albanes@yahoo.com.mx>> wrote:

From: Luis Albanes <ing_albanes@yahoo.com.mx<mailto:ing_albanes@yahoo.com.mx>>

Subject: [MW:5198] NDT after PWHT
To: materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>
Date: Thursday, 20 May, 2010, 7:00 PM

Dear friends
We just finished PWHT in an LPG sphere acording to ASME VIII section I, and I can´t find in the code the part that obligues to Xray after this treatment, any one has experience with this? where does ASME VIII say it has to be done?
Thank you
Luis Albanés

--
To post to this group, send email to materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com<mailto:materials-welding-unsubscribe@googlegroups.com>
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.


--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Filtered by Hosted Filtering


--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

By Materials & Welding
Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...
Post a Comment
Read more