In the case of 30 mm plate, the carbon is marginally less and you can negotiate with your customer. In case of any other enquiry, visit http://blog.weldwell.com for free advice.
S.N.Bagchi,
Editor, Blog.weldwell.com & welding fraternity
-----Original Message-----
From: Tran Van Vuong <vuong.tv@gmail.com>
To: materials-welding@googlegroups.com
Sent: Mon, 18 Jan 2010 11:48 am
Subject: [MW:4074] RE: 4073] RE: 4072] composition manganese less than requirment of ASTM A36
-- From: Tran Van Vuong <vuong.tv@gmail.com>
To: materials-welding@googlegroups.com
Sent: Mon, 18 Jan 2010 11:48 am
Subject: [MW:4074] RE: 4073] RE: 4072] composition manganese less than requirment of ASTM A36
Thank you very much,
Please advice me for detail as blow:
Plate 20mm
Plate 30mm
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Pablo Acelajado
Sent: Monday, January 18, 2010 12:09 PM
To: materials-welding@googlegroups.com
Subject: [MW:4073] RE: 4072] composition manganese less than requirment of ASTM A36
Sent: Monday, January 18, 2010 12:09 PM
To: materials-welding@googlegroups.com
Subject: [MW:4073] RE: 4072] composition manganese less than requirment of ASTM A36
January 18, 2010
Hello Tran!
You did not mention the value that you are getting but only indicated that it is lesser than the lower limit. If all other tests are OK, then you need to discuss the matter with your customer for a concession so that it will be accepted.
Thanks.
PJA
SAVE TREES - THINK BEFORE YOU PRINT
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Tran Van Vuong
Sent: Monday, January 18, 2010 6:53 AM
To: materials-welding@googlegroups.com
Subject: [MW:4072] composition manganese less than requirment of ASTM A36
Importance: High
Sent: Monday, January 18, 2010 6:53 AM
To: materials-welding@googlegroups.com
Subject: [MW:4072] composition manganese less than requirment of ASTM A36
Importance: High
Dear All,
Please help me in PMI testing for material ASTM A36 thickness over 20.0mm, the composition requirement of manganese is (0.8 – 1.2)%. But result of test is less than 0.8%. Other testings are accepted (tensile, bending, elongation).
Please advice me this result is accepted or not.
If not, please advice the solution.
Thank you in advance.
TRAN VAN VUONG
-- To post to this group, send email to materials-welding@googlegroups.com To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com For more options, visit this group's bolg at http://materials-welding.blogspot.com/ The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment