Hi Mr Ali Asghari,
It’s the voltage which critically affects the flux consumption. More flux would get consumed is the voltage is high; accordingly the composition of welds would be affected. See the attached document (page-2) for illustration.
Thanks
Pradip Goswami.P.Eng
88,Garth Trails Crescent
Hamilton,Ontario, L9B2X1,Canada
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Ali Asghari
Sent: Monday, January 25, 2010 12:40 PM
To: materials-welding@googlegroups.com
Subject: Re: [MW:4147] FW: 4106] essentials about SAW PROCESS
Dear Goswami
thank you for reply.
but my intention of question is :when the composition of weld metal is dependent to flux,which welding parameters affect on amount of alloying elements in weld metal?
regards
From: pgoswami <pgoswami@quickclic.net>
To: materials-welding@googlegroups.com
Sent: Sun, February 21, 2010 3:04:18 AM
Subject: [MW:4116] FW: 4106] essentials about SAW PROCESS
Mr Asghari,
Both QW-404.10 & 404.27 applies to procedure qualification by SAW and are essential variables. In SAW , one can do the alloying through flux only, or though wire or through flux and wire combined.
You may be aware that SAW fluxes are manufactured (briefly without going into details) as acidic flux, basic (agglomerated, bonded or fused) or neutral fluxes. Each flux behaves differently during welding. Due to these factors SAW flux is so important and fabricator has to know precisely the AWS classification as mentioned in SFA -5.23 or SFA 5.17 as provided by consumable manufacturer.
QW 404.10- Where the alloy content of the weld metal is very much dependent upon the composition of the flux used, any change in any part of the welding procedure may result in the important alloying elements in the weld metal being outside of the specification range given in the Welding Procedure Specification. If the production welds are not being made in accordance with the procedure specification, the authorized inspector may require that a check be made on the chemical composition of the weld metal on a production weld.
QW-404.27— Where the alloy content of the weld metal is largely dependent upon the composition of the supplemental filler metal or any other form of additive, such as alloy powder. This changes weld metal chemistry thus deemed as essential variable as per ASME Sec-IX.
Regarding your earlier queries:-
· what is effect of filler composition in transfer mode in GMAW?—None, transfer mode is a function of, wire size, shielding gas and Polarity/ Arc Current.
· why backing material is required for FCAW for root pass?—FCAW is not meant to be a full penetration weld , unless some improved and special power source is used, such as STT.
Hope I have tried to clear your doubts. I am attaching an e-book on SAW for your reference.
Thanks
Pradip Goswami,P.Eng ,IWE
Senior Engineer/Specialist(Welding-Metallurgy)
Machine Dynamics & Component Integrity Dept.
Engineering & Training Services Division
ONTARIO POWER GENERATION Inc.
PO Box-2000, RR-55(South)
Nanticoke, Ontario,N0A1L0
Tel:-(519) 587-2201, Ext 3107--in Nanticoke
(416) 231-4111, Ext 5925--in Kipling,Toronto
Fax: (519) 587-6814
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of ali asghari
Sent: Wednesday, January 20, 2010 5:35 AM
To: materials-welding@googlegroups.com
Subject: [MW:4106] essentials about SAW PROCESS
Dear all
does anybody have experiences or interpretations about
QW 404.10 & 404.27(the alloy content of the weld metal is largely dependent(how can assess) upon the composition of the flux used, any change in any part of the welding procedure which would result in the important alloying elements in the weld)
QW 404.24:10% VOLUME IN TOTAL LENTGH OR NOT?
1
REGARD ADVANCES.
THIS MESSAGE IS ONLY INTENDED FOR THE USE OF THE INTENDED RECIPIENT(S) AND MAY CONTAIN INFORMATION THAT IS PRIVILEGED, PROPRIETARY AND/OR CONFIDENTIAL. If you are not the intended recipient, you are hereby notified that any review, retransmission, dissemination, distribution, copying, conversion to hard copy or other use of this communication is strictly prohibited. If you are not the intended recipient and have received this message in error, please notify me by return e-mail and delete this message from your system. Ontario Power Generation Inc.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment