Re: [MW:32219] Stabilization heat treatment

Hi,

It is same ordinary WPS like others.

There will be only addition to heat treatment @ 900 degree C for four hours soaking time followed by air quenching (cooling I'm open air). 

Thanks,

Rajnish Dixit

Sent from Yahoo Mail on Android

On Fri, 2 Apr 2021 at 8:44, K.M Hrishikesan

<hrishikm07@gmail.com> wrote:

Hi..Need a small help.

Does  anybody have an established WPS for stabilization heat treatment?

MOC:

 ASTM A 358 TP 347

Specimen thickness is 25 mm.

Thanks.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAFHBd__iMawJ0FOuy0xRBiCp3ZHr%2BfhFSjuHgkbP4ZrLM-ndCg%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/149233260.441800.1618159572731%40mail.yahoo.com.