Dear Mr. Shankar,
Could you please sent some more information?
Can you inform us what kind of stainless steel you applied.
What welding process you used, and which filler material.
Is it plate or tube welding.
What kind of water ( is there any chlorid in the water) did you use for hydrotesting and did you air test before hydrotesting.
What kind of defects did you see on the X-ray?
After this we might be able to give an answer on your question.
bets regards,
Dick Overkleeft EWE
Bureau Veritas
2011/12/24 Dinesh Ravi Shankar <dinesh_ravi2001@yahoo.com>
--Dear friends,During hydro testing of stainless steel, recently 2 tests leak occurred at welded joint area. I verified RT films, PMI reports...etc.Just I want to find root cause.Please advise me that what proactive surveillance need to take of further hydro test failure & how it is happening..?Thank you & Best Regards,
S. Dinesh Ravi Shankar.
Mechanical Inspector,
Saudi Aramco Project Inspection Division (SAPID),
Manifa Core Hydrocarbon Facilities Project.Kingdom of Saudi Arabia.,Mobile : +966 568059765,
Tel : +966 3 379 2018.
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment