Re: [MW:12552] Uncontrolled heating and cooling effect of Carbon steel below lower critical temperature

Dear all,

In my openion, the PHASE will remain the same with variation in GRAIN SIZE with respect to its cooling rate. Heating rate will not make any difference.

reg,
JJ




--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

Re: [MW:35507] WPS for Furnace PWHT

As per ASME B31.3, Clause 331.1.6 (b): Any required PWHT shall be carried out in accordance with the qualified WPS. For furnace PWHT inv...

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...
  • WELD AND WELDING SYMBOLS
    Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...