Hi,Your WPS will make as per ASME or API???--On Fri, Aug 28, 2020, 18:17 <pgoswami@rogers.com> wrote:--Hi KK,
What's the design code ? ASME Sec VIII , DIV-1 or ASME B-31.3. Looking at the text below, it sounds Sec VIII, DIV-1 is the design code.
Look at this curve and the exemption clauses for more clarifications. If this curve exempts BM/thickness from impact test , then weld/HAZ should be exempted from impact also.
Thanks.
Pradip Goswami, P.Eng, IWE
Consultant-Welding-Metallurgical Engineering
Cell & Whatsapp-905-9793232.
From: materials-welding@googlegroups.com <materials-welding@googlegroups.com> On Behalf Of K K
Sent: August 28, 2020 6:45 AM
To: Materials & Welding <materials-welding@googlegroups.com>
Subject: [MW:31360] Re: As per ASME Sec IX Ed. 2019, ASME Sec VIII, Div-1 and API RP 582
Dear Experts,
Can I get a response from you?
According to ASME Sec.8, and MDMT is 5°C.
Please send me your valuable reply to my doubts.
Thanks and Regards
KK
On Wednesday, August 26, 2020 at 9:47:06 AM UTC+5:30 K K wrote:
Dear Experts,
Impact testing requirements for Equipment Anchor Chair to top plate/wash welding, base plate, and plug welding.
According to ASME B31.3 above 25mm impact test required.
So for that, I have restricted to my thickness range 5.00mm to 25.4 mm in WPS.
But Now my requirements for welding Equipment Anchor Chair to top plate/wash welding, base plate, and plug welding. up to 32.88 mm,
For the 32.88 mm thickness, I have to conduct an impact test or not required impact test
Process - SMAW.
P No - P1.Gr.No- 1 to P1 Gr,1/2
Thickness range - 5.00 mm to 32.88 mm.
Material - ASTM 516 Gr.60 to ASTM Gr.70
As per ASME Sec IX Ed. 2019, ASME Sec VIII, Div-1, and API RP 582according to mentioned code required Impact test or not?
Thanks in advance
Regards
KK
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/49f11814-bb8f-434c-8da9-9551a4ad71a9n%40googlegroups.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/!%26!AAAAAAAAAAAuAAAAAAAAABVPzeizzeRJsiPziIE5jXQBAMO2jhD3dRHOtM0AqgC7tuYAAAAAAA4AABAAAACyN7NuThHkQ6frJxXVPdcwAQAAAAA%3D%40rogers.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CA%2Ba0BHbqmnvj7bPyvzHkFS_uf5wEVqXB3yjmTHhWtBfowVGb3w%40mail.gmail.com.
KIRAN
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAMFjUk4anJKhc8sJTaVM-OONF3vc2sswyzMX%3DQpsQ_OwU6W%3D2Q%40mail.gmail.com.
No comments:
Post a Comment