[MW:19056] -40F (-40C) impact qualification of 1-1/4Cr 1/2Mo (P4)

I have a customer requiring -40F (-40C) impact qualification for 1-1/4Cr 1/2Mo material (ASME Sc IX).  Design and fabrication is required to be in accordance with ASME Sc. VIII, Division 1.  Weld thickness is approximately 1-3/4 in. (45mm).  It is anticipated that only SAW and SMAW will be required.  While I have a number of procedures qualified at -20F (-29C) it would appear that they are approaching the DBTT for the weld metal and HAZ in most instances.  I would like to know if anyone has qualified 1-1/4Cr 1/2Mo to -40 and what special measures were taken to achieve it;  i.e special filler metal requirements or specific filler metal employed, special weld techniques or parameter restrictions, etc.  Materials are SA-387 Grade 11 Class 2 and SA-182 F11 Class 2.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...