Re: [MW:17608] RE: 17605] Impact test for A106

Pgoswami

 

I think the question PVT was asking was, is the impact test required for the type of piping material weld joints? and if so at what temperature, I think the temperature range specified in his mail was not 0 to -150 but 0-150C he was not asking which piping materials would be best suitable, but the answer is yes the impact test is required for the weld joints and the ideal temperature should be -20

 

Very Best Regards

Behrooz Alavi

From: pgoswami <pgoswami@quickclic.net>
To: materials-welding@googlegroups.com
Sent: Monday, May 6, 2013 2:34 PM
Subject: [MW:17607] RE: 17605] Impact test for A106

Hello PVT,

 

Usually A/SA 106 is not a reliable material for design temperature  below -20 DegC. If the use of C-Mn steel is insisted  A/SA -333 Gr-6 would be the choice. By definition , materials falling under this specification( A/SA-333 ) are meant for low- temperature applications.

 

If the lowest design temperature is -150 DegC( as mentioned below), then the choice should be austenitic S.S grades, 304L or 316L by default.

 

Thanks

 

Pradip Goswami,P.Eng.IWE

Welding & Metallurgical Specialist

Ontario , Canada .

Email-pgoswami@sympatico.ca,

pgoswami@quickclic.net

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of PVT
Sent: Monday, May 06, 2013 6:19 AM
To: materials-welding@googlegroups.com
Subject: [MW:17605] Impact test for A106

Dear Experts,

 

Process piping with material A106- thickness = 35 mm, design temp: 0 - 150 °C . My question: As per ASME B31.3, impact test for weld joint is required or not? If required, what temperature to impact test?

 

Thanks!

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
 
 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.