[MW:2780] Re: 2742] Weld Crack at Root trough weld metal

Hi, 7018 is not for first pass, 6010 does
 
Luis Albanés

--- El mar 21-jul-09, Yadav Shiva <luvshiv2002@gmail.com> escribió:

De:: Yadav Shiva <luvshiv2002@gmail.com>
Asunto: [MW:2760] Re: 2742] Weld Crack at Root trough weld metal
A: materials-welding@googlegroups.com
Fecha: martes 21 de julio de 2009, 23:25


Hi Varmazyar,
                     Yes we can use 6010 or 7018 at root.But i our
case , why it happened , why crack came ??
Regards,
YC.Shiva,
QA/QC Engg,
Doha Qatar,
+974 6166465.
On 7/22/09, Ali Varmazyar <av-ssg@msa.ir> wrote:
>
> Surry, I forget to talk about your service. if your service is sour then you
> must consider Nace MR0175/ISO15156-2 requirements too.
>
> Best Regards
>
> A.  Varmazyar
>
> MSA -Welding Engineering Department
> Msa,Arak,Markazi,IRAN - P.O. 148
> Tel.: +988612172725~6
> Fax: +988612172702
>
>
> -----Original Message-----
> From: materials-welding@googlegroups.com
> [mailto:materials-welding@googlegroups.com] On Behalf Of shiva
> Sent: Tuesday, July 21, 2009 6:04 PM
> To: Materials & Welding
> Subject: [MW:2742] Weld Crack at Root trough weld metal
>
>
> We are using API 5L X65 grade material for sour environment. With
> reference to our WPS we used (Ador electrodes) e 8010 for root and
> 8018 for hot fill pass.
> We took NDT and its okay. But after 1 month 4 weld joints crack. We
> checked the macro hardness for existing and cracked joint . There was
> a high hardness eg 351, 329 on root and in weld metal cap side 280
> above. Which is very high.
>
> Can you please tell me for this material what type of electrodes to be
> used? And why this occoured ?? And what may be possible reason for
> this occourance?
>
> Regards,
> Y.C.Shiva,
> QA/QC Engineer,
> +974 6166465
> Doha Qatar.
>
>
>
> >
>


¡Obtén la mejor experiencia en la web!
Descarga gratis el nuevo Internet Explorer 8.br> http://downloads.yahoo.com/ieak8/?l=mx --~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

[MW:35346] Cast-iron welding

Any advice for cast iron welding Sent from Yahoo Mail for iPhone

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...