[MW:2742] Weld Crack at Root trough weld metal

We are using API 5L X65 grade material for sour environment. With
reference to our WPS we used (Ador electrodes) e 8010 for root and
8018 for hot fill pass.
We took NDT and its okay. But after 1 month 4 weld joints crack. We
checked the macro hardness for existing and cracked joint . There was
a high hardness eg 351, 329 on root and in weld metal cap side 280
above. Which is very high.

Can you please tell me for this material what type of electrodes to be
used? And why this occoured ?? And what may be possible reason for
this occourance?

Regards,
Y.C.Shiva,
QA/QC Engineer,
+974 6166465
Doha Qatar.

--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---