Ayhan,
you must have finished this work. What did you do later?
Prepared thorough repair WPS?
Regards,
Huey
On Sunday, July 24, 2011 1:09:08 PM UTC+8, Ayhan GEDUK wrote:
Dear All,
We have x60 base material (+3mm cladded with Inconel 625) CRA pipeline.
If there is any defect at the root we have to cut-out.
Company specification is +100 mm each side cut back, that means 200 mm length.
Normally they have to be remove HAZ area 15 mm each side.
When we are sending our material for destructive test they are getting 10 mm away for to get base material hardness.
I am going to Deviation Request but I needed to get international standards reference.
API 1104 and ASME B.31.8 does not mention this subject.
Is there anyone got the related matter.
I will stay looking forward to hearing from you soon.
Thanking you very much in advance,
Ayhan Gedik
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
No comments:
Post a Comment