Re: [MW:15931] Welding CS to SS ? THICKNESS > 19 mm

Dear Zakaria,

Really not required, as the process involved is for C.S. material & for some other reason of joining on other side requirement is for S.S. 316L by further process requirement for purpose of reaction involved.

Also for PWHT for C.S. is after 32 mm Thk. (Exception is forming operation above 16mm thk.-like dished end.)

 

If at all still customer wants PWHT, THEN LIMIT UP TO 400 deg C. & longer soaking period.

Hope matter is largely clear.

Best Regards,
C.B.KAPADIA
0091 98926 33442

---

From: Zakaria ghrab <zakaria.ghrab@gmail.com>
To: materials-welding@googlegroups.com
Sent: Wednesday, 14 November 2012 1:09 PM
Subject: [MW:15928] Welding CS to SS ? THICKNESS > 19 mm

Dear experts,

  We have one doubt. Need your help.

We have to weld carbon steel (A106-C)  to austinitioc stainless steel (316 L  grade), thickness > 19 mm.

PWHT in this case is mandatory ? if yes, they're   some restrictions ?


Regards.

--

زكرياء غراب
GHRAB Zakaria

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.