Re: [MW:30567] PWHT

MOC : SA 240 Gr 316L

Service: WET sour/H2

On Thu, Feb 27, 2020 at 8:54 AM 'james gerald' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Interesting. What is the material and process Fluid service.

Thanks & Regards

J.Gerald Jayakumar

On Wednesday, February 26, 2020, 09:58:25 PM GMT+7, prateik tolani <tolaniprateik@gmail.com> wrote:

Dear Experts,

one of our client is asking for Solution annealing for complete vessel

vessel size - 1300 ID x 6500 mm long, thickness 8 mm with lots of nozzles.

whether it is possible.

at higher temperature of 1100 Deg C and rapid cooling in water, vessel will distort completely.

Tolani 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAGNY-_B7ijqhsdu07O8_05RXO4bHD8%3D%2BGpUx9W68j--H_ZMXQQ%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/363187691.817747.1582770708416%40mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAGNY-_B9%2BfnKLyWjZr6X1fWB4UTv_Ccc7k2ae36BD2H5FyTkdw%40mail.gmail.com.