Re: Re: [MW:29788] Orbital TIG – welding Machine

By Materials & Welding
Hi Azam,

I was retriving the documents and its been more than 3 years , so i couldnt retrive as fast but i recollected the scenario and the machines.

I beleive it is ''OTTO ARC AUTOMATIC WELDING MACHINE''

I retrived WPS too which is 22mm thickness in which 6 goes for GTAW manual and 22 for GTAW automatic.

Now after reading my past emails, i retrived the scenario that my sub contractor had some issues during WQT, where the machine automatically turned off in which we did not entertained WQT approval, hence i dont suggest with my machine in which i went through which is not acceptable and conluding that i dont recommend orbittal based in my experience.

My last email was for SAW machine in which we had GTAW+GMAW+SAW which was fine quality with production which is of miller.

Yours
MOHAMED MUNEEB MAHABOOB
+91-786-700-444-6      TRZ - INDIA

''Scrutiny is that scrutiny is the best scrutiny - where you solely alone to go for all micros from macros''






    






muneebslsa@gmail.com
 
Sender: Mohd Azam
Send Time: 2019-07-06 12:31
Subject: Re: [MW:29782] Orbital TIG – welding Machine

Good Day !!

 

We are looking for new Orbital welding Machine with GTAW Process. 100 % RT is to be done on weld joint so no compromise with regards to quality of weld, If you have used automatic welding machine, Kindly suggest machine Brand and Model.

 

Appreciate your feedback @ earliest.

 

 

Best regards,

Mohammed Azam

Doha- Qatar


On Fri, Jul 5, 2019 at 8:46 AM muneebslsa@gmail.com <muneebslsa@gmail.com> wrote:
Hi,

You're already having one or looking for one? Orbital?

We did back before three years, productivity wise i cannot guarentee, but quality wise its ok when you dont have defects and strengths are acceptable, so confirm what youre into?

Thanks,

Yours
MOHAMED MUNEEB MAHABOOB
+91-786-700-444-6      TRZ - INDIA
''quality is not your cup of tea to waive as per your own business conditions - quality is that tree fixed firmly deep rooted, in which each root is an evidence of references''


Sender: Mohd Azam
Send Time: 2019-07-02 19:11
Subject: [MW:29773] Orbital TIG – welding Machine

Hi,

 

We are looking for Orbital TIG welding machine- Automatic, If anyone using this machine with proven result with regards to quality and productivity. Machine shall be capable for Root and Fill and cap pass welding. The joint details which is to be executed as below:

 

Coil welding        CS Material Size 4" x sch. 40 – Pipe to Elbow        Clearance between pipe to elbow around 85 mm

 

 

Thanks in advance to share the details.

 

 

Best regards,

Mohammed Azam

Doha-Qatar

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CABD%2BRXTuo-m98R2srnenam_iYmx4RCP7JHpHPoPBbAqwyUHYVg%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/2019070510541648678611%40gmail.com.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CABD%2BRXTFhG6tetdqdw1P3Z66_6jEctvQZ4mcsULF47STDkfrZg%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

Comments

Post a Comment

Popular posts from this blog

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

By Materials & Welding
Hi,  You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this.  Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime.  Again, these simulated no. Of cycles shall be specified in MTC.  The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case).  One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example.  In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more