Re: [MW:25241] Pitting corrosion test failure

At what temperature was it carried out..and holding time?

Sent from my iPhone

On Aug 11, 2016, at 02:23, Prasu Cutie <pracuty@gmail.com> wrote:

Dear experts,

We had pittng corrosion failure in duplex stainless  steel 2205
Process: GTAW
Thk: 7.62mm
Filler: ER2209
Product: pipe
Heat input observed: 1.5 to 2.5kj
Gas: argon 99.9997purity
Weight loss reqd is <4g/sq.mtr, achieved 21g/sq.mtr
Testing is done as per ASTM G48

Can any one tell me why this failure occured, what could be the reason?

Regards
Prasad

--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAKgcArS8ogq8UVK8TnByOg9L7Garxaej2a1pwHyQ8iR9MeSRuQ%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.