Since the material description indicates as a ltcs material ,hence it is must to have a impact test in low temperature ( Considered under extreme condition of the particular location) ,moreover if it is for low temperature application then heat treatment will be required also ,as per good engineering practice and asme 31.3 ....others please correct me if you find it incorrect please.
-- Regards
Pratish
On Friday, January 2, 2015 4:02:27 PM UTC+5:30, saravanan sornam wrote:
On Friday, January 2, 2015 4:02:27 PM UTC+5:30, saravanan sornam wrote:
Hi experts
Happy new year to all of u.
I have a query.
When we use A333 Gr.6 pipe as a Swage Transition Nozzle , specified in BOM in Fabrication Dwg, which is a noncoded item and exempted from impact test,
When i reviewed any requirements in ASME Sec II part A, A333 Gr.6,
I could not find any special requirements like Heat treatment after forming to transition, any special product marking, any special testing etc.
If you have any info related to my above queries then please do share.
Regards
Sarav.
Korea
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/f4b90fe8-fe7e-431c-b527-c4baa0aee829%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.
Comments