Hi
What type of joint are you talking about ?
If it is a single sided joint without access from other side, root + hot pass has to be welded by TIG. You cant use SMAW directly.
If there is access from other side and chip back is possible you can go for SMAW like double V full penetration joint..
Also you can weld partial penetration joint root with SMAW..
Regards
Prem Nautiyal
On Fri, 16 Oct 2009 11:50:08 +0530 wrote
>
Hi there,
One of our manager wants to Develop WPS for SS which can utilize
SMAW –root. I do not see it is common in SS welding. But there may be something
can make us competitive against GTAW root.
Does anybody have thought to share with me?
Thanks in Advance..!
Minal Patel
PREM S NAUTIYAL
CELL : 9820313278
 |
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
S355 J2 WP is a weathering structural steel It has better atmospheric corrosion resistance. Use E 8018 - W1/W2 Electrodes This is regular...
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-
Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
No comments:
Post a Comment