Dear , any defects open to the surface normally to be attended , as good engineering practice , but if you adhere strictly to code for acceptance , no body will cross
Decision is yours
Thanks & Best Regards,
Vinayak Kale
E & C DIv. QA & I , OGSP
Larsen And Toubro Ltd
Powai , Mumbai
vinayak_kale@lntenc.com
Ph No.+91- 67053805/3685
Fax No. +91-67051988
(M) - + 91 9892743803
| asad azmi <azmiasadayub@gmail.com> Sent by: materials-welding@googlegroups.com 09/28/2009 01:05 PM
|
|
GOODMORNING...........
can anybody can confirm whether a pin hole of diameter 3mm and depth of approximately 5 mm in fillet weld of 6mm of material SA 516GR 70 can be VISUALLY accepted. The vessel is fabricated as per ASME SEC VIII DIV 1.
If YES then by which code.
Kindly note that if we consider acceptance crieteria for PT/MT, as per ASME SEC VIII DIV 1, APPENDIX 6/8, Rounded indication upto 4.8mm is acceptable.
can the above defect can be accepted on the basis of acceptance crieteria of PT/MT.
please reply ASAP.
Thanks & Regards
Asad Azmi
On Thu, Sep 24, 2009 at 1:35 PM, Adi <adinraos@gmail.com> wrote:
If joint repair came in 2" pipe, it is very difficult to identify
repair the exact location & root repair we can't do, so the joint
should be cut out
My question is When we are calculating the welders repair % we have
to consider total length of 2" is repair ? Why because we repaired the
total length
Is it correct please advice
Adi
Disclaimer :This email and any files transmitted with it are intended solely for the use of the addressee(s) only and may contain confidential and/or privileged information. If you are not the addressee, then this message is not intended for you and be advised that you have received this email in error and that any use , dissemination , forwarding, printing or copying of this email is strictly prohibited. In such case please notify the sender and delete this email and any attachments with it from your system immediately.Receipt of this email by you shall not give rise to any liability on the part of Larsen & Toubro Limited
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
No comments:
Post a Comment