[MW:3295] Welding qualification of very low sulfur steels.

----- Forwarded Message ----
From: kannan_cit <kannan_cit@yahoo.com>
To: piping_valves@yahoogroups.com
Sent: Wednesday, September 23, 2009 7:26:46 PM
Subject: [piping_valves] Welding qualification of very low sulfur steels.

 

Quit some time ago, I was having great difficulty in finding mills manufacturing steels with sulfur limited to 0.001% max. due to a wrong prescription by one of the well known PMC. Though it was resolved with higher relaxation later, I started to look into the issues concerning the restrictions posed in the sulfur content in steels, which were mainly added to increase the machinabilty, in various applications including the H2S/Sour service applications. The article in the link provides an insight in welding a low sulfur material.

The issue in the context of welding is that, while sulfur content is reduced the surface tension is reduced resulting in wider concave welds with lesser penetration, which pose a problem in thick walled pipes which are common in sour services. The insert ring solution proposed in the link below may solve the problem of higher weld penetration, which calls for different weld procedure. Similar to ASME BPE standard's prescription of limitation on, weld sulfur with appropriate quality check, does such requirement called in the BPV.

I seek our member's suggestion on the subject of welding procedure qualification, in such applications where sulfur content is restricted from 0.002% to 0.010% in sour/H2S applications.

http://www.thefabri cator.com/ tubepipefabricat ion/tubepipefabr ication_article. cfm?ID=533

With regards,
Kannan

__._,_.___
Recent Activity
Visit Your Group
Give Back

Yahoo! for Good

Get inspired

by a good cause.

Y! Toolbar

Get it Free!

easy 1-click access

to your groups.

Yahoo! Groups

Start a group

in 3 easy steps.

Connect with others.

.

__,_._,___


--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...