[MW:2246] Re: Y COFFICIENT IN PIPING

By Materials & Welding
Dear Ali,
You see, without going in to much theory, I surmised from what you gave in the parenthesis as follows:
If the strength goes down with increase in temp , you will need more thickness, naturally, as compared to when you operate at low temp. I hope this clears it.
Rgds,
Shank

--- On Wed, 27/5/09, Ali Asghari <asghariali@rocketmail.com> wrote:

From: Ali Asghari <asghariali@rocketmail.com>
Subject: [MW:2244] Re: Y COFFICIENT IN PIPING
To: materials-welding@googlegroups.com
Date: Wednesday, 27 May, 2009, 3:10 PM

dear Shank Vagal
can you explain more?because my point of view from writting parenthesis is the required minimum thickness (with assuming constant work presure)decreases.
rjd

From: Shank Vagal <nach_sam@yahoo.com>
To: materials-welding@googlegroups.com
Sent: Wednesday, May 27, 2009 11:18:34 AM
Subject: [MW:2241] Re: Y COFFICIENT IN PIPING

The answer you have given in the parenthesis itself..............

--- On Wed, 27/5/09, Ali Asghari <asghariali@rocketmail.com> wrote:

From: Ali Asghari <asghariali@rocketmail.com>
Subject: [MW:2240] Y COFFICIENT IN PIPING
To: materials-welding@googlegroups.com
Date: Wednesday, 27 May, 2009, 10:49 AM

CAN ANY BODY EXPLAIN,WHY Y (IN B31.3 FOR CALCULATING THICKNESS) INCREASES WITH INCREASING TEMPRATURE?
(ACCORDING TO ALLOWABLE STRESS DECREASES WITH INCREASING TEMP) 
 
REGARD ADVANCE




Explore and discover exciting holidays and getaways with Yahoo! India Travel Click here!



Cricket on your mind? Visit the ultimate cricket website. Enter now! --~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more