[MW:2233] Re: CHEVRON CRACK

dear ahank vagal

thank you for response.

but because H.I of SAW IS MORE than SMAW ,therefore the time is existed for diffusion out H from base and weld metal.as a result the propability of occurance for chevron crack is lower than smaw.

regard advance

From: Shank Vagal <nach_sam@yahoo.com>
To: materials-welding@googlegroups.com
Sent: Saturday, May 23, 2009 1:44:53 PM
Subject: [MW:2231] Re: CHEVRON CRACK

My dear Ali,

1. Heat Input is not the highest in SAW but in more SMAW.

2. On Cheveron Cracking, please see a brief from some of my notes.

Chevron cracking: This type of cracking is unfamiliar in process piping and is mainly confined to thick-wall multipass welds deposited in carbon and carbon-manganese steels and is associated with fabrication of pressure-retaining facilities and heavy structural fabrications. The cracking mechanism is attributed to mishandled / sloppily stored submerged arc flux, which has, therefore, been allowed to absorb moisture. During welding, this moisture dissociates into hydrogen and oxygen. The oxygen may form oxides within the weld, or recombine and evaporate. Hydrogen gets trapped within the weld metal as it cools down and, if a sufficient quantity of hydrogen is available, cracking is likely to occur. The cracks take the shape of a chevron or a V, hence the name chevron cracking.

Hydrogen or stress are known to trigger these crack (HIC, SCC)..

The marks are formed in brittle failures in plates due to the way the fast moving crack front propagates along the plate as illustrated in the fig.

The "chevron" marks point to the crack origin.

The exact thickness limits for this behaviour are connected with the fracture toughness of the steel, temperature, etc., depending on the

specific steel and its condition.

 However, a common NDE may not be able  to readily detect or determine a steel's / process's susceptibility to these cracks. To find if a steel is sensitive to this, you must use fracture toughness  measurement methods like CTOD, etc.

Note : Please see attachment for the fig, I can not post it here.

Best regards,

Shashank Vagal

--- On Sat, 23/5/09, Ali Asghari <asghariali@rocketmail.com> wrote:

From: Ali Asghari <asghariali@rocketmail.com>
Subject: [MW:2228] CHEVRON CRACK
To: materials-welding@googlegroups.com
Date: Saturday, 23 May, 2009, 9:37 AM

IN FABRICATION SPECIFICATION OF MY PROJECT SAID THAT:FOR THICKNESS ABOVE 25mm IN SAW,WELD SHALL BE EXAMINED FOR DETECTION OF CHEVRON CRACK BY ULTRASONIC.

ACCORDING TO HEAT INPUT IN SAW IS HIGHER THAN SMAW,WHY IT SAID ONLY IN SAW?

Own a website.Get an unlimited package.Pay next to nothing.* Click here!.

--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...

Materials & Welding

Search This Blog