[MW:2167] RE: 2163] Determination of Et value in IBR Regulation 271

Use of permissible working stress from ASME Section II D or other code is acceptable to IBR as per clause no 343.

Also one observation is that Clause 350 and 271 does not call for stress values to be determined as per clause 16 (d).

 

Regds/Jignesh

---

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of desaid@toyoindia.com
Sent: Tuesday, May 12, 2009 3:18 PM
To: materials-welding@googlegroups.com; piping_valves@yahoogroups.com
Cc: dhwani0608@yahoo.com
Subject: [MW:2163] <Security Level 2>Determination of Et value in IBR Regulation 271

Dear Sirs,

Under IBR regulation 271, it is stated that allowable stress shall be considered lower of E_t/1.5 or R/2.7.

Here, E_t is - Yield Point (0.2%proof stress) at temp. t..

Can any one say from where this Et value shall be taken.
There are two options :

1. Refer IBR 16 (d) which gives table listing the values of Ratio ofEt/R20 for different temperatures. From which we can compute Et for particular temp. t.
(This table is only for carbon steel in general). Shall Et value be computed from this?

2. Or from Table Y-1 of ASME Sec. II-D? Which lists the yield strength at different temp. materialwise.

Kindly help on this issue as early as possible.

Pls. mark reply to piping_valves id also as i don't receive mail from materials-welding group.

Thanks in advance,

Regrds,
Dhwani
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---