[MW:2272] Re: Pl.Help.

By Materials & Welding
Abhijit ,
Thanks for u r responce,it gives me lots of moral support & if u find any supporting stds.pl. mail me.
Thanks & Regards,
Prashant 

--- On Thu, 28/5/09, abbey kangale <abhianu12@yahoo.com> wrote:

From: abbey kangale <abhianu12@yahoo.com>
Subject: [MW:2269] Re: Pl.Help.
To: materials-welding@googlegroups.com
Date: Thursday, 28 May, 2009, 3:48 PM


Prashant
 
I am sorry to say ;their is no such ref standards available in Market which specify Quantum of Inspection Levels
 
At this stage you can issue Inspection reports for all valves mentioneing subject to Acceptance of selected Inspection Levels from your End User/Engineering Consultancey
 
You can issue Inspection report with all your observation and your Inspection Level assumptions but mention clearlycceptance by Client due to unavailbility of QAP/Inspection levels
 
I know this is regularly happens in India with TPI companies and they have to take thier own judgement for their Inspection and isuue Inspection reports with conditional approval.and for that your management has to agree for same .
 
Abhijit  
--- On Thu, 5/28/09, prashant pansare <prashantpan_99@yahoo.co.in> wrote:

From: prashant pansare <prashantpan_99@yahoo.co.in>
Subject: [MW:2267] Pl.Help.
To: materials-welding@googlegroups.com
Date: Thursday, May 28, 2009, 1:11 PM

Dear all,
I' ve inspected ball & NRV ( API 6D)  valves for xyz company.QAP was not available & client also not provided extent of check,but i inspected Hydro test 100% for body & 10% foe seat & released all the valves after satisfactory results.
My firm wants clarification for Why i not done 100% testing for seat also?
I' ve been warned,badly as i' ve carried out inspection without QAP & taken my own decision.
Is there any specs. or std. to rsolve this matter? & if available pl.forward me,so that i can
responce immediately to avoid further action.
Pl. help.
Regards to all ...PRASHANT    

Explore and discover exciting holidays and getaways with Yahoo! India Travel Click here!

Explore and discover exciting holidays and getaways with Yahoo! India Travel Click here! --~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more