CHECK THE IMPACT TESTED COUPON FROM THE LAB AND MEASURE THE VALUE
REGARDS
PARAG
On Nov 1, 2012 3:40 PM, "Ankit PAtel" <ankit.patel@orientalindia.net> wrote:
>
> Dear Experts,
>
>
>
> We have performed a PQR for 25 thk plate , P1(SA 516 GR-70 ) To P8(SA 240 TP-316L). These PQR has been stress relieved at 620° C & impact tested at -20°C.
>
> The testing laboratory has noted down only the joule values for the impact test, but they have not noted the Lateral Expansion Values P-8 Material.
>
> The Avg. Joules Values observed are as follows:
>
> Weld-72.67 J
>
> HAZ(GR-70)-35.33J
>
> HAZ(GR-316L)-158 J
>
> PARENT(GR-70)-51.33J
>
> PARENT(GR-316L)-298 J
>
>
>
> Now our TPI says that for GR-316L Lateral Expansion Values is must for acceptance of the PQR.
>
> Is it so?
>
> Or based on these joules values these PQR can be accepted & used for weld having requirement of impact test at -20°c
>
>
>
>
>
> Thanks & Regards
>
> Ankit Patel
> Engineer Quality
>
>
>
>
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at http://materials-welding.blogspot.com/
> http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
>
> The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
>
>
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment