Re: [MW:8092] CS and SS

 
CS and SS shall not be mixed and shall not come into contact with each other - 
 
 Reason when both SS and CS stocked together, carbon steel debris, particles, or scales will stick to the SS surfaces. Girinding particles from carbon steel will also fall on SS surfaces. These foreign particles or debris are have high carbon content and have anodic properties.   Anodic materials or particles can be corroded away easily, or you can say corrosion will start on the SS materials because of this carbon particles (it is obvious that carbon steels are prone to be corroded, if not painted). These foreign matters deposited on SS surfaces can create pitting corrosion on SS surfaces. Simply saying oxidation on SS will start because of this foreign matters or debris on carbon steels.
 
That is why most spec demands separate storage area and fabrication area for CS and SS.
 
CS and Alloy steels -  this also should not be mixed. but here corrosion is not the reason.  You cannot distinguish between CS and Alloy steel visually as both looks same. and you cannot identify which is CS and which is AS unless you have some marking or colour coding system. Both have equal affinity to corrosion. That is Colour coding of Alloy steels are must.
 
Thanks
 
Murugesan
Mcconnell Dowell SEA pte ltd
Singapore

On Fri, Nov 5, 2010 at 4:53 PM, srinivas rao <ksrvasu@gmail.com> wrote:
Hi ,


Can anyone pls let me know the reason why SS and CS should not mixed? Is it the same for CS and Alloy Steels???

Thanks and Regards

Srinivas

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34916] Applicability of Impact requirement as per ASME B31.3

Dear All, Design code – ASME B31.3, Welding Code- ASME BPVC SEC IX Material  to be used used during Fabrication - SA 333Gr6 (P No.1 G...