Hi Ahmed,
We also suffer a lot of rejection for Super DUplex with same reason of COrrosion, Its better to revise the Gas mixture combination and control of heat inputs ..
Welding environments effects as well, Just arrange the area dust free ,humidity free. 

Regards,

Muhammad Azeem Iqbal
Welding Inspector Aramco Approved
053110-8577/0554453626/0590071467




On Mon, 19 Sept 2022 at 09:33, ahmad elsharkawy <ahmad.sharkawy88@gmail.com> wrote:
Could you please what happen after that and what is the parameter you used to pass the corrosion test?

On Thursday, January 2, 2014 at 4:24:01 PM UTC+3 tan billy wrote:


Dear Experts,

I have try to qualified repair procedure  14'inch superduplex pipe 30 mm thickness(UNS32750) where using purging and shielding gas 98% Ar and 2% N2.Unfortunately I failed on the pitting  corrosion testing(35⁰C)5g/m2 weigh loss(test required 4g/m2)G48 method A. Original weld pass at 0gram weigh loss. Piting was found at side(near excavation area) and root weld where the side of test piece is more severe . Heat input for root around 1.2KJ/mm and the rest passes are 0.8-1.1kjmm. Filler wire used is ER2594.

 

a)Can you guys provide information for the purging usually used( I am using only span), suitable environment for welding superduplex? 

b)Do we need to cut off the tip of the filler wire if it is oxidized(reused wire)?

c) Can we use power brush for interpass cleaningexclude capping?

d.) The deposite thickness is thin for every pass in order to get high travel speed/low heat input?

e)  I am using cleaning agent acetone to clean the bevel , does this matter?

  Please let me know if any goes wrong.

 

Weld details

1.)    Single V joint

2.)    Sample extract from to position. Welded 6G position.

3.)    Repair procedure. Excavation up to 6mm root ligament where as per drawing.

4.)   

5.)    Pitting corrosion picture

6.)    Interpass temperature <100⁰C

7.)    Oxygen level <50ppm, excavation method grinding.

8.)    Interpass cleaning, power brush.

9.)   

10.)

 

 


--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/1a90017f-edd2-4937-9c2f-4e65decd9b06n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAHqH7yD3p7Hu2crBrW9B%3DSfCeM2ggv7si2dfX%2BzfqUooEPTP5Q%40mail.gmail.com.

Comments

Popular posts from this blog

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

Hi,  You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this.  Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime.  Again, these simulated no. Of cycles shall be specified in MTC.  The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case).  One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example.  In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...