Dear Gerald Sir,

Greetings!!

Please advise the dimensions of the test plate.

300 mm (W) x 500 mm (L) is enough.

In our case one test plate is required for each welding procedure used for Cat. A & B Joints.

80 mm thick dish heads are manufactured with a single joint - PTC is required for these joints.

Thank You & Regards

Williams P Wilson

+968-94600828

QA/QC Engineer

Please consider the environment before printing this message

On Tue, Oct 4, 2022 at 1:14 PM Sezgin Ckllı <euniversty@gmail.com> wrote:

Thank you Mr. Gerald.

Believe me, you've been very helpful.

Thanks & Regards
Sezgin ÇAKALLI

4 Ekim 2022 Salı tarihinde saat 06:20:02 UTC+3 itibarıyla gerry_tup şunları yazdı:
Figure (1)

Weld (Thickness 15mm)

1 set with notch in the weld 1.5mm from the top surface (SAW Process)
If GMAW weld metal greater than 2.5mm, 1 set in GMAW weld subsize

HAZ

1 set from 1/4t to 1/2t in SAW HAZ
If GMAW weld metal greater than 2.5mm, 1 set in GMAW HAZ subsize

Figure(2) 50mm

Weld

1 set 1.5mm from the surface with the notch in the SAW weld
1 set below the GMAW weld in the SAW weld near to centerline and notch in SAW weld
If GMAW weld metal greater than 2.5mm, 1 set in GMAW weld subsize

HAZ

2 sets in HAZ as per table 84.6
If GMAW weld metal greater than 2.5mm, 1 set in GMAW HAZ subsize

Figure (3) 35mm

Weld

1 set with notch in the weld 1.5mm from the top surface (SAW Process)
1 set with notch in the weld 1.5mm from the root surface (GTAW Process)subsize

HAZ

2 sets in HAZ as per table 84.6
If GTAW weld metal greater than 2.5mm, 1 set in GTAW HAZ subsize

Thanks & Regards
J.Gerald Jayakumar

On Monday, 3 October, 2022 at 02:43:51 pm GMT+4, Sezgin Ckllı <euniv...@gmail.com> wrote:

That's why we subjected it to the impact test.
What I want to learn is how many samples should be taken from where in the sourced material I want to specify below?

I will be glad, if you inform me.

Yours truly

3 Ekim 2022 Pazartesi tarihinde saat 12:43:30 UTC+3 itibarıyla gerry_tup şunları yazdı:
When Impact testing is a design requirement as per ASME Sec.VIII Div.I, production Impact testing is required. Only Impact test is the requirement as per ASME Sec.VIII Div.I unless other tests are required by your Client Requirement.

For production Impact test follow below section.

For any specific requirement as per below table, please describe in detail what clarification you require.

Thanks & Regards
J.Gerald Jayakumar

On Monday, 3 October, 2022 at 12:05:30 pm GMT+4, Sezgin Ckllı <euniv...@gmail.com> wrote:

Thank you Mr. J. Greald

But as far as I have learned, please pay attention to the following paragraph and confirm its accuracy.

**
Regards

Sezgin ÇAKALLI
s.cak...@gmail.com
3 Ekim 2022 Pazartesi tarihinde saat 07:43:02 UTC+3 itibarıyla gerry_tup şunları yazdı:
UG-84

Thanks & Regards
J.Gerald Jayakumar

On Monday, 3 October, 2022 at 08:22:28 am GMT+4, Sezgin Ckllı <euniv...@gmail.com> wrote:

We design a pressure vessel according to ASME VIII Div.1 and our customer request shows "Production test plates according to Code requirements". Can you tell us the section showing where we can take samples from materials that vary according to their thickness. Or I need someone to contact me about the issue.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/3ff85526-0de0-44a3-b2f3-6ec89fe81124n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/6278e0fc-2cf7-4528-a601-534d5a421c02n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/e213243d-1b70-4c51-99ae-f9bc26d494fen%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/e38ad76c-ec2e-41fb-96a0-073cdcb02d10n%40googlegroups.com.