Dear Venkatesan
Can you tell me what is your work Application, as per my knowledge some welding consumables have a natural tendency to crack due to high hardness if the crack is transverse, then no problem & please tell me which welding consumable you use & how much hardness its give as welded?
With Regards |
Rahul J Rathod |
mob +91 9727076573 |
whats up +91 81155889118 |
Email : welder.tigarc6g@gmail.com |
On Mon, 29 Apr 2019 at 12:47, <srimasstech@gmail.com> wrote:
DEAR EXPERTS--WHILE HARDFACING DONE IN PTA WELDING OVER CN3MN MATERIAL WE FOUND SMALL (3-4 MM LENGTH) CRACKS IN EVERY WHERE.PLEASE GUIDE US WHAT ARE ALL THE PRECAUTIONS WE CAN MADE BEFORE WELDING ?REGARD'SM.VENKATESANSRIMASSTECHCHENNAI
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment