[MW:29489] Re: welder qualification

By Materials & Welding
REFER THIS ALSO As per ASME B31.4

434.8.4 Welding Standards. All the welding done
under this Code shall be performed under a specification
that embodies the minimum requirements of this Code
and shall encompass the requirements of API 1104
except as provided in paras. 434.8.3(a) and (b).
434.8.3 Welder and Welding Procedure
Qualifications
(a) Welder and welding procedure qualifications for
cross-country pipelines shall be performed in accordance
with API 1104. Welder and welding procedure
qualifications for alloy steel and for shop fabricated piping
assemblies, and welding at stations and terminals
shall be performed in accordance with API 1104 or
Section IX of the ASME Boiler and Pressure Vessel Code.
(b) Prior to anywelding covered by this Code, awelding
procedure specification shall be established and
qualified by testing to demonstrate that welds having
suitable mechanical properties and soundness can be
produced. Welding procedure specifications shall be
qualified as required by API 1104, or Section IX of the
ASME Boiler and Pressure Vessel Code, whichever is
appropriate for the locations, materials, and type of
welding to be performed except as modified by the
following

On Saturday, 27 November 2010 13:11:38 UTC+3, bas karan wrote:

Dear all

for welder qualification can we use sec IX instead of 1104 for cross country pipelines.

if no ,what is the issue behind?

Regards
Baskaran.



--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

Comments

Post a Comment

Popular posts from this blog

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

By Materials & Welding
Hi,  You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this.  Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime.  Again, these simulated no. Of cycles shall be specified in MTC.  The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case).  One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example.  In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...
Post a Comment
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more