Tube failure in S&T HE


Tubes at the tube sheet at hot air inlet have brittle fractured and cracked. This may be due to either 

 1)  Thermal shock /loading 

       or   

 2) Chloride stress cracking due to water quality above 50 ppm in chlorides . 



No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...