SS type 410 is a P-No 6 material? so the min temp. for PWHT as per Section VIII-1 is 760 degC. However, PWHT is not required for that grade when the conditions of note (a) - Table UHA-32-1 are met.
You are invited to read carrefully the 1st paragraph of UCL-34, especialy if you have welded with an austenitic filler metal
Στις Παρ, 5 Απρ 2019 στις 9:28 π.μ., ο/η Vijay Katkar <katkar.vijay22@gmail.com> έγραψε:
Hi All,--Need your suggestion.Is it ok if we do Dual PWHT after 625 weld overlay on SS410 material.First PWHT- 685 for 8.5 hrs.Second PWHT- 660 for 8.5 hrs.Kindly suggest.Thank youVijay Katkar
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
Dr. Georgios Dilintas,
Dipl. Ing. In Aeronautic and Space Engineering
Ph.D in Mechanics of Solids - Computational Mechanics
A.I.S, A.N.I, IRCA Lead Auditor
Welding, Stress Analysis, Corrosion, QA/QC, Failure Analysis, Risk Analysis
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment