[MW:26391] Re: Requirement of Solution Annealing for SS DIshed head after forming

Hi,

Please let me know What is the finishing forming temperature as per UHA-44.

Thanks,

Vipul

On Tuesday, 13 September 2011 15:48:03 UTC+5:30, asad azmi wrote:
Dear All,
 
Greetings.
 
SS Vessel is being fabricated as per construction code - ASME SEC VIII DIV 1
 
SERVICE : SOUR Service
 
Material of Construction  for Dished Head - SA 240 316L, 20 mm Thickness.
 
I  believe stresses will be  induced in the material  during forming and as a result , Sulfide Stress Cracking (SSC) failure may occur during operation.
 
Whether Solution Annealing of SS Dished Head is required after forming?
 
Please give reference of any International Standard.
 
Thanks & Regards
 
Asad Azmi

--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/aaab94b5-9f51-44cf-98e3-2624725d6e2f%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

[MW:35346] Cast-iron welding

Any advice for cast iron welding Sent from Yahoo Mail for iPhone