Re: [MW:23730] Cellulosic Electrode Usage Instead of Basic Electrode

Since Hydrogen level ( Around 30 to 60 ppm), it is not recommended for multiple pass/higher thick material because we will end up HICC

THANKS & BEST REGARDS,

KG.PANDITHAN, IWE,  AWS-CWI, CSWIP 3.1,

CONSULTANT-WELDING & QUALITY

On Sat, Oct 17, 2015 at 1:51 PM, Perumal Govindan <perumalgovindan@gmail.com> wrote:

Hi

You can not replace the electrode, since SFA number, UTS & alloying element presence to meet the weld metal properties  and WPS (approved) for pipe welding.

Regards
PG

On 17 Oct 2015 11:51, "Demir Alp" <demiralp85@gmail.com> wrote:

• Dear Sirs;

  I would like to get Your professional advisory regarding selection of the filler material in Piping Welding of the P:1 G:1 Pipe Materials.

  For a large variety of Thickness and Diameters i have written 3 different WPS by combination of GTAW + SMAW process with usage of ER 70S-6 (Root and Hot Passes using GTAW) and E7018 (for Fill passes and Cap using  SMAW process.)

  However Our construction dept , insists on usage of Cellulosic electrodes instead of basic electrodes for higher deposition rate.

  As QA/QC I am doubtful replacing 7018 with 7010 or any other cellulosic electrode because of their tendency for hydrogen induced cracking. I'd like to add in my previous project We used to have X70 pipes and our employer didn't allow us to use cellulosic elecrodes just because hydrogen induced cracking.

  Thus I would like  to get your professional opinion regarding this subject,

   Best Regards; 

  Demir

• 
  

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/4783eb1a-1cc3-41df-8a2e-9700b07dc15b%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CANiuf9fUf-DEFKzGiM4S3HM6TWqdrn8Q-wd4DBf%2BdkBiNJNo0A%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eNtjmcBxebbqyNCxatwbMqBoP5U-qmX08st-aFtiB_vig%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.