[MW:23613] FW: NEED ADVISE CORROSION IN INHIBITOR TANK REGD

Hi Neileshkumar,

What're the surrounding operating or environmental conditions around the tank. Are there any acid fumes involved. Looks like this tank was not insulated at all??? Is that true.

Appreciate more information on the operating conditions.

 
Thanks


 
Pradip Goswami, P.Eng,IWE
Welding & Metallurgical Engineering Specialist
Hamilton, Ontario, Canada
pgoswami@quickclic.net
pradip.goswami@gmail.com
ca.linkedin.com/pub/pradip-goswami/5/985/299

-----Original Message-----
From: Neilash Kumar [mailto:neilashkumar@yahoo.com]
Sent: Tuesday, September 29, 2015 2:45 AM
To: Pgosami Sir; Pgosami sir
Subject: NEED ADVISE CORROSION IN INHIBITOR TANK REGD

Dear Sir,

Good Morning, please find the attached tank drawing fabricated by us for our client & it is corroded fully , Can you please clarify,

1. Why the tank are corroded So fast?
2. Can you please advise us the method to stop /reduce the rate of corrosion by applying a top coat &  what type of coating to be applied?

please advise me . Material is 316L tank.

Regards
P.Neilashkumar

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...