Dear experts,
We're going to construct a new power station; according ASME sect B31.1.
We have many alloy steels (Grades P11, P91, P22 material) welded joints. Even when PWHT is performed, our client say that we don't have to perform hardness test.
Even NDE is the client scope, i'm searching for support from code to have exact infiormation, uis it mandatory ?
Need your help.
Regards.
--
SDEM Entreprises
-- We're going to construct a new power station; according ASME sect B31.1.
We have many alloy steels (Grades P11, P91, P22 material) welded joints. Even when PWHT is performed, our client say that we don't have to perform hardness test.
Even NDE is the client scope, i'm searching for support from code to have exact infiormation, uis it mandatory ?
Need your help.
Regards.
--
زكرياء غراب
GHRAB Zakaria
Site QA/QC ManagerGHRAB Zakaria
SDEM Entreprises
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment