Re: [MW:8963] Clarrification regarding Material Inspection

Anand,

First you need to get it clarified whether it is for Upstream or for refinery. The applicable standard for upstream is NACE MR0175 and for Refinery it is NACE MR 0103.

Normally we need to check the products Heat Treatment Form and the Hardness plus the chemistry as it is specified for stainless steels.

J.GERALD JAYAKUMAR 00919344954677

--- On Mon, 12/27/10, AnandM@punjlloyd.com <AnandM@punjlloyd.com> wrote:

> From: AnandM@punjlloyd.com <AnandM@punjlloyd.com>
> Subject: [MW:8959] Clarrification regarding Material Inspection
> To: materials-welding@googlegroups.com
> Date: Monday, December 27, 2010, 3:03 PM
>
> Dear All,
> Pls Clarify, what are the characteristics to verified for
> Sour service
> material inspection. Kindly mention any important point to
> be check.
>
> With Regards
>
> Anand.M
>
>
>
>
> ---------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
>
>
> This e-mail and any files transmitted with it are for the
> sole use of the intended recipient(s) and may contain
> confidential and privileged information. If you are not the
> intended recipient of this communication, we request you to
> notify the sender immediately by return email and destroy
> all copies and the original message. Any unauthorized
> review, use, disclosure, dissemination, forwarding, printing
> or copying of this email is strictly prohibited. The
> recipient acknowledges that Punj Lloyd Limited or its
> subsidiaries and associated companies (collectively "Punj
> Lloyd Group") are unable to exercise control or ensure or
> guarantee the integrity of/over the contents of the
> information contained in e-mail transmissions and further
> acknowledges that any view, opinion or advice expressed in
> this message are those of the individual sender and no
> binding nature of the message shall be implied or assumed
> unless the sender does so expressly with due authority of
> Punj Lloyd Group. Although we have taken all
> reasonable precautions to ensure that this communication is
> free from viruses. We do not assume responsibility for any
> loss or damage arising from the use of this email.
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at http://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members
> personel views and meant for educational purposes only,
> Users must take their own decisions w.r.t. applicable
> code/standard/contract documents.
>

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...

Materials & Welding

Search This Blog