[MW:1348] Re: 1334] WPS combination of two PQRs

Dear Friends,

Please note as per Clause QW200.4(b) of ASME IX, these PQR's cannot
be combined.

Only When the "T" ≥ 13mm in both the PQR's, then the combination of
PQR's are allowed

In addition to the above

when impact is required :

Please note as per QW-403.5 combination of PQR'S are allowed when
both the qualification records have the same essential & supplementary
essentials except the basemetals assigned with different group Nos.
within the same P. No.

When impact is not required :

These qualification records with basemetals of different Group Nos.are
allowed to combine.

Regards,
K.S.Rameshkumar,
Sharjah
00971505080853

On Nov 24, 11:50 am, "Bathula Raghuram \(Mumbai - PIPING\)"
<R.Bath...@ticb.com> wrote:
> QW403.5 and 403.6
>
> ________________________________
>
> From: Sukamal Naskar [mailto:sukamalbec...@gmail.com]
> Sent: Monday, November 24, 2008 1:19 PM
> To: materials-welding@googlegroups.com
> Subject: Re: [MW:1336] RE: 1334] WPS combination of two PQRs
>
> Thanks for your response.
>
> Can you please let me know according to which clause of ASME Sec-IX, the
> base material thickness is 10mm to 16mm with impact. Why not 8mm to 20mm
> ( combination of two PQRs)
>
> Regards
>
> With impact testing
>
> Any material combination can be welded within range of 10-16mm base
> metal thickness
>
> Sorry, There was a mistake here P1G1 can't be welded using SMAW process
>
> ________________________________
>
> From: materials-welding@googlegroups.com
> [mailto:materials-welding@googlegroups.com] On Behalf Of Bathula
> Raghuram (Mumbai - PIPING)
> Sent: Monday, November 24, 2008 1:06 PM
> To: materials-welding@googlegroups.com
> Subject: [MW:1336] RE: 1334] WPS combination of two PQRs
>
> Without impact testing
>
> 1.5 to 16mm base metal thickness can be welded.
>
> With impact testing
>
> Any material combination can be welded within range of 10-16mm base
> metal thickness
>
> ________________________________
>
> From: materials-welding@googlegroups.com
> [mailto:materials-welding@googlegroups.com] On Behalf Of Sukamal Naskar
> Sent: Monday, November 24, 2008 11:36 AM
> To: materials-welding@googlegroups.com
> Subject: [MW:1334] WPS combination of two PQRs
>
> Friends,
>
> Good afternoon. I need one help regarding one WPS, combination of two
> PQRs.
> the 1st PQR is 8mm thick, with base material SA 516Gr.70 ( P No.1 Gr. 2)
> with SA 516 Gr.65 (P No.1 Gr.1). welded with full GTAW process , and is
> impact tested at -29 deg. C.
>
> 2nd PQR is 10mm thick, with base material SA 516Gr.70 ( P No.1 Gr. 2)
> with SA 516 Gr.70 (P No.1 Gr.2). welded with full SMAW process , and is
> impact tested at -29 deg. C.
>
> If we combine these two PQRs to make one WPS for the combination welding
> process GTAW & SMAW, will the base material thickness range will be 8 mm
> to 20mm ( with impact) and 1.5 mm to 20mm (without impact) ?
>
> The deposited weld metal thickness for GTAW will be 16 mm max. and SMAW
> 20mm max. ( for both with / without impact)
>
> And if the impact test is required at - 29 deg. C, can we use this WPS
> for all possible base material combinations ( P1 Gr.1 to P1Gr.1; P1 Gr2
> to P1 Gr2 and P1 Gr.1 to P1 Gr.2) ??
>
> Regards
>
> --
> Sukamal Naskar
> MMHE ATB
> +60177007205
> Malaysia
>
> --
> Sukamal Naskar
> MMHE ATB
> +60177007205
> Malaysia

--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---