Pl. send MTCs of both the materials 

On Thu, Apr 8, 2021 at 2:51 PM Pravin Poornachandran <htcispravin@gmail.com> wrote:

Dear Expert,

We are doing a weld joint with following base metal combination: 

SM490 weld to railway (alloyed, high tensile material) 

I used E7016 for this welding, after 4 hours, crack was observed on the weld toe,

however there is no crack on the weldment, thus I assume this is cold crack. 

Crack was noticed on the railway material, not on SM490A material. 

Welding condition:

Baking was done 300-350degC x 1hr 

thickness: 16mm both material 

Preheat: 200degC 

Post heating: 250degC x 1hr

Can anyone advise how to solve this crack defects

Best regards,

Pravin Poornachandran

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADDyn7eE6%2Ba9MxkOJQ6oTfKK3xFXmLvXGn0yp5cFjAzWpGt_-A%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADder3M8d3M7Q1bU0QyJ_%2BS74ftXamPZoCsuYdPM6mjk7vfMWQ%40mail.gmail.com.