Dear all,

hope all members are fine, 

Our company is fabricating a Mud Tank. the client requirement that RT-3 will be performed. I want only one question: how much RT film is used in this tank if the total weld length is 32 meter and its RT reference code for satisfying the client.

this tank as per API standard.

and reference will be API.

On Mon, Sep 7, 2020 at 3:57 PM 'james gerald' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Specify your Design code as RT-3 is applicable only for Pressure vessels fabricated of ASME Sec VIII 

Thanks & Regards

J.Gerald Jayakumar

On Monday, 7 September, 2020, 05:45:43 pm GMT+7, Andrew Ubakwem <andyubakwem@gmail.com> wrote:

Dear Ghulum,

I seems not to understand your query because either your English composition is confusing me the more or I do not get basis for your questions.

Question#4: weld length 32mtr? 

Please clarify.

Regards,

Andrew.

On Mon, Sep 7, 2020, 11:30 AM Ghulam Mustafa <gmt.lah@gmail.com> wrote:

Dear All,

Hope all member will be fine,

I have a many question about RT,

1. What we can use RT level on Tank?

2. Reference of RT level in ASME Section VIII Div-I ? or any other reference standard (API/ASME) except Section V. 

3. If tank design by API Standard, can we use ASME VIII Div-I reference for RT?

4. If weld length of but weld joint is 32 mtr, as per RT-3, how much 6" film are required as per code.  

Please guide me in short and proper words that we can under stand.

Best Regards

Regards,

GMT

Save life| Don't destroy nature | Help save paper

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/3561e869-1bdd-4112-bf46-b0e86b82f936n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAK1J--PJywc9C74tnwRd0wct3it7bZJWKme%2BV0-nTEKP-%2BVe2Q%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/827203294.3042464.1599475710206%40mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAHnLYCJYpjLbbMAjEbZhrDoBHh6ZpQb%2BA5TGzuatwhn%2B-YD-Nw%40mail.gmail.com.